排号

Grade No.

LX245  BRIGHT

相对粘度

Relative viscosity

FZ/T 51004-2011

25℃ , 96%H2SO4

/

2.50

熔体质量流动速率

Melt mass-flow rate

GB/T 3682.1-2018

235℃, 2. 16kg

g/10min

32.8

拉伸断裂应力

Tensile breaking stress

GB/T 1040.1-2022

50mm/min

MPa

67.45

断裂伸长率

Breaking Elongation

GB/T 1040.1-2022

50mm/min

%

99.95

弯曲强度

Flexural strength

GB/T 9341-2008

2mm/min

MPa

89.99

弯曲模量

Flexural modulus

GB/T 9341-2008

2mm/min

MPa

2014.10

悬臂梁缺口冲击强度

Izod notched impact strength

GB/T 1843-2008

23℃/5.5J

kJ/m2

3.16

含水率

Water content

Q/1500LXJXA001-2023

/

%

0.038

熔 点

Melting point

Q/1500LXJXA001-2023

Heating rate

10℃/min

℃

226.9

密 度

Density

GB/T 1033.1-2008

/

g/cm3

1.165

说明：以上数据为对应牌号产品典型数值，供客户产品选择参考，实际值以收到产品的检验报告为准。 Disclaimer: The above figures are typical values for the corresponding series of product, served as reference for customer's selecting products, and the actual values are subject to COA of  the product.